Effect of sucralfate against hydrochloric acid-induced dental erosion

Abstract

Objective

Devising effective measures for the prevention of hydrochloric acid (HCl)-induced erosion is of great significance. This is even more important in dentine, in which products have limited diffusion. Therefore, agents that can bind to proteins forming an acid-resistant gel-like coat, such as sucralfate, may stand out as a promising alternative. This study investigated the protective effect of sucralfate suspensions against HCl-induced dental erosion.

Materials and methods

In the first experiment, hydroxyapatite (HAp) crystals were pre-treated with a commercial sucralfate suspension (CoSS, pH 5.9), a stannous-containing sodium fluoride solution (NaF/SnCl2 pH 4.5), two prepared sucralfate suspensions (PrSS, pH 5.9 and 4.5), or deionized water (DI, control). HAp dissolution was measured using a pH-stat system. In a subsequent experiment, embedded/polished enamel and root dentine slabs were allocated into five groups to be treated with one of the tested substances prior to and during erosion-remineralization cycles (HCl-2 min + artificial saliva 60 min, two times per day, 5 days). Surface loss was assessed profilometrically. Data were analyzed by ANOVA and Tukey's tests.

Results

HAp dissolution was as follows: NaF/SnCl2 < CoSS < PrSS/pH 4.5, while PrSS/pH 5.9 = DI and both did not differ from CoSS and PrSS/pH 4.5. In enamel, surface loss did not differ between CoSS and PrSS/pH 4.5, with both having lower surface loss than PrSS/pH 5.9 and DI and NaF/SnCl2 differing only from DI. In root dentine, surface loss was as follows: CoSS < PrSS/pH 5.9 < (NaF/SnCl2 = DI), while PrSS/pH 4.5 = CoSS = PrSS/pH 5.9.

Conclusion

Sucralfate suspension provided anti-erosive protection to HCl-induced erosion.

Clinical relevance

Sucralfate may protect teeth against erosion caused by gastric acid.