Different surface modifications combined with universal adhesives: the impact on the bonding properties of zirconia to composite resin cement

Abstract

Objective

The purpose of this study was to analyze the impact of plasma treatment and (universal adhesives) UAs on the bonding properties of zirconia.

Material and methods

Zirconia specimens (N = 744; n = 186/pretreatment) were prepared, highly polished, and pretreated: (i) plasma (oxygen plasma, 10s, 5 mm), (ii) airborne-particle abrasion (alumina, 50 μm, 0.05 MPa, 5 s, 10 mm), (iii) airborne-particle abrasion + plasma, and (iv) without pretreatment (highly polished surface). Surface roughness (Ra) and surface free energy (SFE) were measured (n = 6/pretreatment). Tensile bond strength (TBS) specimens (n = 180/pretreatment) were further divided (n = 18/conditioning): Clearfil Ceramic Primer (PCG), All-Bond Universal (ABU), Adhese Universal (AU), Clearfil Universal Bond (CUB), G-Premio Bond (GPB), Futurabond U (FBU), iBond Universal (IBU), One Coat 7 Universal (OCU), Scotchbond Universal (SBU), and no conditioning. PCG was luted with Panavia F2.0 and the remaining groups with DuoCem. After storage in distilled water (24 h; 37 °C) and thermocycling (5000×; 5 °C/55 °C), TBS was measured and fracture types (FTs) were determined. Data were analyzed using univariate ANOVA with a partial eta square (ƞP2), the Kruskal–Wallis H, the Mann–Whitney U, and the Chi2 test (P < .05).

Results

Plasma treatment resulted in an increase of SFE but had no impact on Ra. Airborne-particle abrasion resulted in the highest Ra and a higher TBS when compared with plasma and non-treatment. SBU and AU obtained a higher TBS when compared with PCG. OCU, FBU, ABU, IBU, and GPB indicated comparable TBS to PCG. CUB revealed the lowest TBS.

Conclusions

Plasma treatment cannot substitute airborne-particle abrasion when bonding zirconia but MDP-containing adhesives are essential for successful clinical outcomes.

Clinical relevance

Airborne-particle abrasion with a low pressure (0.05 MPa) in combination with UAs promotes the clinical success of adhesively bonded zirconia restorations.



http://bit.ly/2SOhC5m